PLASTICIZED GRANULES FOR INSULATION OF ELECTRICAL CABLES

Plasticized granules for electrical cables are recommended for general purpose insulation and sheeting or with special properties such as high flame retardance, resistance of low temperature, high temperature etc.

Appearance, shape, sizes and colour of granules :

The granules have an homogenous appearance, cylindrical or lenticular shape, sizes up to max. 5 mm (max. 4% granules above the limit or agglomerated are acceptable). The granules can be natural or coloured as customer's requirement.

Packing :

The granules are packed in polyethylene bags of 30 kgs, in polyethylene bags repacked in polypropylene bags of 30 kgs or big bags of 750 kgs.

Storage and transport of granules :

The granules are stored in closed, dry warehouses, far away of direct UV action, at a distance of minimum 2 m from any heating source; the storage temperature is recommended to be from +5⁰C up to +40⁰C.
The granules must be kept min. 24 hours at room temperature before the processing.
The transport of granules is done by covered means of transport.

Technical properties of granules :

Tehnical properties of granules are shown in the tables. The values shown in the tables are the result of tests made on specimens, got in conformity with test methods, specific to each characteristic; these values are not the values of the characteristics got on finished product, obtained from granules.
Connections can be done with international standards (DINVDE 0207, GOST 5960) at customer's requirement.

Types			I 80	I 88	I 88-13	IF*	I₂
Applications			General purpose insulation up to 1 KV			Flame retardant insulation up to 1 KV	Insulation for power cables up to 6 KV
Technical characteristics	UM	Test method	Values
Density	g/cm³	STAS 5886	1,25-1,35	1,25-1,35	-	1,30-1,40	1,31-1,41
Density	g/cm³	ISOR 1183	-	-	1,25-1,35	-	-
Hardness at 23+2⁰C	⁰ShA	STAS 8643	78+4	87+4	-	91+4	-
Hardness at 23+2⁰C	⁰ShA	ASTMD 2240	-	-	88+3	-	-
Thermal stability at 180⁰C	minutes	BS 2782 met 130A	min 150	min 150	-	-	-
Thermal stability at 200⁰C	minutes	BS 2782 met 130A	-	-	min 100	min 100	min 150
Tensile strength	N/mm²	STAS 6642	min 14	min 18	-	min 20	min 15
Tensile strength	N/mm²	ASTMD 638	-	-	min 17	-	-
Elongation at break	%	STAS 6642	min 250	min 220	-	min 200	min 150
Elongation at break	%	ASTMD 638	-	-	min 200	-	-
Low temperature resistance	⁰C	STAS 7014	-30	-30	-	-20	-
Low temperature resistance	⁰C	ASTMD 746	-	-	-20	-	-
Volume resistivity at 23⁰C	Ohmcm	STAS 6107	min 1*10¹³	min 2*10¹³	-	min 1*10¹⁴	-
Volume resistivity at 23⁰C	Ohmcm	DIN 53482	-	-	min 2*10¹³	-	-
Dielectric strength	KV/mm	STAS 6257	min 20	min 20	-	min 20	min 25
Dielectric strength	KV/mm	ASTMD 179	-	-	min 19	-	-
Inflammability	seconds	STAS 7015	max 60	max 60	max 60	max 30	max 60

* Type IF is also manufactured to have resistance in humid and dry climate conditions (climate protection T, 1 working category, in conformity with SF 1/94)

Types			I₂F	I₃	I₄	I₅	IM 80-13
Applications			Flame retardant cables insulation up to 6 KV	Flame retardant cables insulation up to 10 KV	Insulation of flexibile cables up to 1 KV
Technical characteristics	UM	Test method	Values
Density	g/cm³	STAS 5886	1,31-1,41	1,35-1,45	1,20-1,30	-	-
Density	g/cm³	ISOR 1183	-	-	-	-	1,25-1,35
Hardness at 23+2⁰C	⁰ShA	STAS 8643	91+4	92+4	78+4	80+4	-
Hardness at 23+2⁰C	⁰ShA	ASTMD 2240	-	-	-	-	-
Thermal stability at 180⁰C	minutes	BS 2782 met 130A	-	-	-	-	-
Thermal stability at 200⁰C	minutes	BS 2782 met 130A	150	150	90	60	100
Tensile strength	N/mm²	STAS 6642	min 18	min 15	min 15	min 18	-
Tensile strength	N/mm²	ASTMD 638	-	-	-	-	min 15
Elongation at break	%	STAS 6642	min 180	min 150	min 280	min 250	-
Elongation at break	%	ASTMD 638	-	-	-	-	min 275
Low temperature resistance	⁰C	STAS 7014	-20	-20	-40	-	-
Low temperature resistance	⁰C	ASTMD 746	-	-	-	-	-20
Volume resistivity at 23⁰C	Ohmcm	STAS 6107	-	-	min 1*10¹²	min 1*10¹³	-
Volume resistivity at 23⁰C	Ohmcm	DIN 53482	-	-	-	-	min 1*10¹³
Dielectric strength	KV/mm	STAS 6257	min 25	min 25	min 20	min 20	-
Dielectric strength	KV/mm	ASTMD 179	-	-	-	-	min 20
Inflammability	seconds	STAS 7015	max 30	max 60	max 60	max 60	max 60

Types			IM 85-13	F	I₆	I 88-14	I 105
Applications			Insulation and sheeting of flexibile cables up to 1 KV		Insulation of telephonic cables up to 1 KV		Insulation of cables with continuous working temperature of 105⁰C
Technical characteristics	UM	Test method	Values
Density	g/cm³	STAS 5886	-	1,20-1,30	1,35-1,45	-	1,25-1,35
Density	g/cm³	ISOR 1183	1,25-1,35	-	-	1,25-1,35	-
Hardness at 23+2⁰C	⁰ShA	STAS 8643	-	73+4	88+4	-	89+4
Hardness at 23+2⁰C	⁰ShA	ASTMD 2240	85+3	-	-	88+3	-
Thermal stability at 180⁰C	minutes	BS 2782 met 130A	-	min 100	min 100	-	min 150
Thermal stability at 200⁰C	minutes	BS 2782 met 130A	min 100	-	-	min 100	-
Tensile strength	N/mm²	STAS 6642	-	min 14	min 18	-	min 18
Tensile strength	N/mm²	ASTMD 638	min 17	-	-	min 18	-
Elongation at break	%	STAS 6642	-	min 250	min 180	-	min 200
Elongation at break	%	ASTMD 638	min 250	-	-	min 250	-
Low temperature resistance	⁰C	STAS 7014	-	-30	-20	-	-20
Low temperature resistance	⁰C	ASTMD 746	-20	-	-	-20	-
Volume resistivity at 23⁰C	Ohmcm	STAS 6107	-	min 1*10¹¹	min 1*10¹⁴	^-	min 1*10¹³
Volume resistivity at 23⁰C	Ohmcm	DIN 53482	min 2*10¹³	-	-	min 1*10¹⁴	^-
Dielectric strength	KV/mm	STAS 6257	-	min 15	min 20	-	min 20
Dielectric strength	KV/mm	ASTMD 179	min 20	-	-	min 20	-
Inflammability	seconds	STAS 7015	max 60	max 60	max 60	max 60	max 60

Types			M 75	M 80	M 1	M 85	M 2
Applications			General purpose sheeting				Sheeting resistant at bad climate conditions
Technical characteristics	UM	Test method	Values
Density	g/cm³	STAS 5886	-	-	1,25-1,40	-	1,25-1,40
Density	g/cm³	ISOR 1183	1,25-1,35	1,25-1,35	-	1,25-1,35	-
Hardness at 23+2⁰C	⁰ShA	STAS 8643	-	-	84+4	-	87+4
Hardness at 23+2⁰C	⁰ShA	ASTMD 2240	75+3	80+3	-	85+3	-
Thermal stability at 180⁰C	minutes	BS 2782 met 130A	-	-	min 100	-	-
Thermal stability at 200⁰C	minutes	BS 2782 met 130A	min 80	min 60	-	min 60	min 60
Tensile strength	N/mm²	STAS 6642	-	-	min 17,5	-	min 17,5
Tensile strength	N/mm²	ASTMD 638	min 16	min 17	-	min 15	-
Elongation at break	%	STAS 6642	-	-	min 250	-	min 225
Elongation at break	%	ASTMD 638	min 300	min 280	-	min 260	-
Low temperature resistance	⁰C	STAS 7014	-	-	-30	-	-25
Low temperature resistance	⁰C	ASTMD 746	-25	-18	-	-18	-
Dielectric strength	KV/mm	STAS 6257	-	-	min 20	-	min 20
Dielectric strength	KV/mm	ASTMD 179	min 20	min 20	-	min 20	-
Loss of plasticizer	%	STAS 5690 met A	-	-	max 3	-	max 3
Inflammability	seconds	STAS 7015	max 60	max 60	max 60	max 60	max 60

Types			M 3	M 70	M 50	M 50 F	M F *	FRSI - 90
Applications			Sheeting for very flexible protection		Low temperature resistant sheeting	Low temperature resistant and flame retardant sheeting		Cable sheeting for working temperature of 90⁰C
Technical characteristics	UM	Test method	Values
Density	g/cm³	STAS 5886	1,20-1,30	-	1,20-1,30	1,20-1,30	1,25-1,33	1,25-1,35
Density	g/cm³	ISOR 1183	-	1,25-1,35	-	-	-	-
Hardness at 23+2⁰C	⁰ShA	STAS 8643	68+4	-	77+4	77+4	88+4	90+5
Hardness at 23+2⁰C	⁰ShA	ASTMD 2240	-	70+3	-	-	-	-
Thermal stability at 180⁰C	minutes	BS 2782 met 130A	min 100	-	min 120	min 120	-	-
Thermal stability at 200⁰C	minutes	BS 2782 met 130A	-	min 50	-	-	min 100	min 100
Tensile strength	N/mm²	STAS 6642	min 14	-	min 15	min 15	min 17,5	min 17,5
Tensile strength	N/mm²	ASTMD 638	-	min 10	-	-	-	-
Elongation at break	%	STAS 6642	min 280	-	min 300	min 300	min 250	min 250
Elongation at break	%	ASTMD 638	-	min 320	-	-	-	-
Low temperature resistance	⁰C	STAS 7014	-40	-	-50	-50	-30	-30
Low temperature resistance	⁰C	ASTMD 746	-	-30	-	-	-	-
Dielectric strength	KV/mm	STAS 6257	min 15	-	min 20	min 20	min 20	min 20
Dielectric strength	KV/mm	ASTMD 179	-	min 18	-	-	-	-
Loss of plasticizer	%	STAS 5690 met A	max 3	-	max 4	max 4	max 3	-
Loss of plasticizer	mg/cm²	STAS 11388/11	-	-	-	-	-	max 1,5
Inflammability	seconds	STAS 7015	max 60	max 60	max 60	max 30	max 30	-
Oxigen index	%	STAS 12321	-	-	-	-	-	min 28

* Type MF is also manufactured to have resistance in humid and dry climate conditions (climate protection T, 1 working category, in conformity with SF 1/94)